Morphology-controllable synthesis and enhanced photocatalytic activity of ZnS nanoparticles

成果简介:Well crystallized cubic sphalerite phase ZnS micro/nanocrystallites were successfully prepared by a facile and efficient microwave hydrothermal method by varying the Zn/S molar ratios. Results show that with Zn/S molar ratio ranges from 2:1 to 1:2, the morphology of the prepared ZnS micro/nanocrystallites changed obviously. ZnS nanoparticles with good dispersibility prepared at Zn/S molar ratio of 1:2, which average size is about 20 nm, shows high photocatalytic activity to degrade Methyl orange (MO). The degradation efficiency of ZnS nanoparticles reaches 97.4% under UV irradiation for 20 min. The good ultraviolet absorbing ability and big specific surface area of ZnS nanoparticles are believed to have a positive impact on improving the final degradation rate and degradation efficiency of MO in our research.

论文引用方式:Yin Lixiong, Wang Dan, Huang Jianfeng, Cao Liyun, Ouyang Haibo, Yong Xiang. Morphology-controllable synthesis and enhanced photocatalytic activity of ZnS nanoparticles[J]. Journal of Alloys & Compounds, 2015.

论文链接:http://www.sciencedirect.com.sci-hub.io/science/article/pii/S0925838815315383

中国硅酸盐学会溶胶凝胶分会

技术支持: 上海维程计算机信息有限公司

Visite : 3214234213 2019 © 中国硅酸盐学会溶胶凝胶分会 版权所有 浙ICP备08101490号-1