Controlled fabrication of ordered mesoporous titania/carbon fiber composites with high photoactivity: Synergistic relationship between surface adsorption and photocatalysis

 

成果简介:Ordered mesoporous TiO2 (OMPT) supported on carbon fibers (OMPT/CFs) were fabricated by supercritical deposition using liquid crystal as soft template. OMPT is dispersed on the CFs with crystalline size of 10–20 nm and pore size of 2–5 nm. Although with increasing amount of TiO2 coatings the surface area of OMPT/CFs decreased relative to that of CFs, OMPT/CFs-n (n = 3) (n is the number of precipitation/drying cycles used to prepare the composite), which had the maximum TiO2 content, still possessed a surface areas of 538.6 m2/g because of the mesostructure characteristics of titania. The OMPT/CFs showed high activity in the photodegradation of AO7 in aqueous solution in comparison with P25, pure OMPT and OMPT–CF mixture. Such activity was facilitated by the synergistic relationship between surface adsorption characteristics and photocatalytic potential. Because of the mutual constraint between loading and surface area on the photocatalytic efficiency, the optimal loading of OMPT in OMPT/CFs-2 for AO7 degradation is 15.2 wt%. The photocatalytic behavior could be described in terms of a modified Langmuir–Hinshelwood model 

 

论文引用方式:Youji Li, Chen Liu, Peng Xu, Ming Li, Mengxiong Zen, Shaohua Tang. Controlled fabrication of ordered mesoporous titania/carbon fiber composites with high photoactivity: Synergistic relationship between surface adsorption and photocatalysis.Chemical Engineering Journal, 243, 2014, 108-116

论文链接:http://www.sciencedirect.com/science/article/pii/S1385894713016318

中国硅酸盐学会溶胶凝胶分会

技术支持: 上海维程计算机信息有限公司

Visite : 3214234213 2019 © 中国硅酸盐学会溶胶凝胶分会 版权所有 浙ICP备08101490号-1