成果简介：Super P was firstly used to enhance the electrochemical performance of SnO2 as anode in Na-ion battery. This composite was prepared by a simple hydrothermal method, exhibiting uniformly dispersed SnO2 nanoparticles on the super P carbon spheres. The SnO2/C nanocomposite could deliver a discharge capacity of 293 mAh g−1 after 100 cycles at a current density of 50 mA g−1. Even at 1000 mA g−1, a capacity of 150 mAh g−1 was still maintained. Further study found that SnO2/super P nanocomposite provided a high Na ion diffusion coefficient and good structural stability during the cycling test. Combining the advantages of low cost and environmental benignity suggest the SnO2/super P composites in this work have great potential as a promising anode for high performance Na-ion battery.

论文引用方式：Yayi Cheng, Jianfeng Huang, Jiayin Li, Zhanwei Xu, Liyun Cao, 

Haibo Ouyang, Jingwen Yan, Hui Qi. SnO2/super P nanocomposites as anode materials for Na-ion batteries with enhanced electrochemical performance. Journal of Alloys and Compounds, 2016, 658, 234-240.

论文链接：http://www.sciencedirect.com/science/article/pii/S0925838815314687